Properties of common rubber types and PVC
|
||
PROPERTIES OF COMMON RUBBER TYPES AND PVC |
||||||||
(1 = excellent; 6 = inadequate) |
NR |
SBR |
BR |
NBR |
CR |
IIR |
EPDM |
PVC |
|
Natural |
Styr. But. |
Butadien |
Nitrile |
Chloroprene |
Butyl |
Ethyl. Prop. |
(Plastomer) |
Breaking strength |
1 |
2 |
4 |
2 |
2 |
3 |
3 |
5 |
Elongation at break |
1 |
2 |
3 |
2 |
2 |
2 |
3 |
5 |
Abrasion resistance |
4 |
2 |
1 |
2 |
3 |
4 |
3 |
4 |
Tear resistance |
2 |
3 |
5 |
3 |
3 |
3 |
3 |
5 |
Cold flexibility |
2 |
3 |
2 |
3 |
4 |
2 |
2 |
6 |
Heat resistance |
4 |
4 |
3 |
3 |
2 |
1 |
1 |
5 |
Weather/ozone resistance |
4 |
4 |
3 |
4 |
2 |
3 |
1 |
2 |
Oil resistance |
6 |
5 |
6 |
1 |
2 |
6 |
6 |
2 |
Acid/base resistance |
3 |
3 |
3 |
4 |
2 |
2 |
1 |
2 |
Flame resistance |
6 |
6 |
6 |
6 |
2 |
6 |
6 |
2 |
US Dimensions&Metrics
|
||
Comparison of RMA and DIN
|
RMA I
|
RMA II
|
DIN Y
|
DIN X
|
Unit
|
Abrasion
|
-
|
-
|
max. 150
|
max. 120
|
mm³
|
Tensile strength
|
min. 17
|
min. 14
|
min. 20
|
min. 25
|
MPa
|
Elongation at break
|
min. 400
|
min. 400
|
min. 400
|
min. 450
|
%
|
Separation strength cover/core
|
-
|
-
|
min. 12
|
min. 12
|
MPa
|
Geometrical tolerances
|
-
|
-
|
Yes
|
Yes
|
|